Kawasuso, Atsuo; Maekawa, Masaki; Fukaya, Yuki; Yabuuchi, Atsushi; Mochizuki, Izumi
no journal, ,
Using spin-polarized positron annihilation spectroscopy, we are studying the spin-polarized state associated with the Heusler alloys. We measured the energy spectrum of annihilation rays by placing the samples and a positron source emitting longitudinaly polarized positrons in magnetic field and extracted the components related to the magnetism. The results imply that (1) the majority spin bands of the CMA sample have a d-like character, (2) those of the CMS sample have more sp-like character and (3) those of the NMS sample have the further sp-like character.
Yamashita, Shinichiro; Kubota, Tomoki*; Oka, Hiroshi*; Hashimoto, Naoyuki*; Onuki, Somei*
no journal, ,
no abstracts in English
Oka, Hiroshi*; Kubota, Tomoki*; Hashimoto, Naoyuki*; Onuki, Somei*; Yamashita, Shinichiro
no journal, ,
no abstracts in English
Saito, Hiroyuki; Machida, Akihiko; Katayama, Yoshinori; Aoki, Katsutoshi; Akiba, Etsuo*
no journal, ,
no abstracts in English
Takeda, Masayasu; Suzuki, Junichi*; Akiya, Takahiro*; Kato, Hiroaki*; Une, Yasuhiro*; Sagawa, Masato*
no journal, ,
no abstracts in English
Matsumura, Daiju; Nishihata, Yasuo; Matsuo, Motoaki*; Li, G.*; Hiyama, Nao*; Semboshi, Satoshi*; Orimo, Shinichi*
no journal, ,
no abstracts in English
Liu, C.*; Chen, S.*; Hashimoto, Naoyuki*; Onuki, Somei*; Shiba, Kiyoyuki; Jitsukawa, Shiro
no journal, ,
Higuchi, Kensuke; Machida, Akihiko; Katayama, Yoshinori; Sakaki, Koji*; Kim, H.*; Nakamura, Yumiko*
no journal, ,
no abstracts in English
Tanno, Takashi; Otsuka, Satoshi; Kaito, Takeji; Yano, Yasuhide; Koyama, Shinichi; Tanaka, Kenya; Oba, Yojiro*; Onuma, Masato*
no journal, ,
The 9Cr-ODS martensitic steel is under development as first candidate material for fast reactor long life fuel cladding. It should have high temperature strength, irradiation resistance and productibility. The 11Cr-ODS steels with additional corrosion resistance by Cr enrichment are also under development. And the evaluation of their applicability for cladding material is in progress. Trial manufacture, creep test and nano/macro structure evaluation of several ODS steels were carried out to modify the chemical composition and manufacturing process of the 11Cr-ODS steel. Uni-axial creep strength of manufactured 11Cr-ODS steels were equal to or higher than that of 9Cr-ODS steel. The strength of 11Cr-ODS steels with 0.3wt% Ti was slightly higher than that with 0.2wt% Ti. The size and number density of dispersed-oxide depended on the amount of added Ti and extra-oxygen.